INTRODUCTION

Humidity contamination is a frequent cause for bonding failure when brackets are bonded with resin composites. For clinical success, these materials need a dry field and enamel conditioning.12 Clinically, enamel contamination with saliva is difficult to control; therefore, less moisture-sensitive materials are always being sought.

For orthodontists, another concern is enamel demineralization that often develops around brackets3–6 within a few weeks.5 Although fluoride mouth rinses are efficient in reducing enamel demineralization,3 the patient's cooperation is essential. Geiger et al7 verified that only 13% of orthodontic patients fully complied with the fluoride rinse protocol. The ideal bonding material should release fluoride, thereby reducing these unfavorable iatrogenic effects of orthodontic therapy.3

The properties of glass ionomer cements (GICs) have enlarged their use in dentistry because of their physicochemical adhesion to enamel even in a wet field28 without acid conditioning.2 In addition, they can release fluoride ions over long periods into adjacent enamel and absorb fluoride from other sources, such as fluoride toothpastes and mouth rinses, thus acting as a rechargeable, slow-release fluoride device.9 This reduces the incidence of decalcification and white-spot lesions around bonded orthodontic appliances.2610 Because of this preventive property, Pascotto et al6 encouraged the use of GICs for orthodontic bonding.

The use of GIC for orthodontic bonding is limited because of its low shear bond strength1112 and high bond failure rates.13 Miguel et al13 verified a bond failure rate of 50.89% for brackets bonded with GIC. The resin-modified glass ionomer cements (RMGICs) have 4 to 6% resinous component.10 This combination results in a material that has GIC's properties with an improved bond strength and has been used successfully for orthodontic bonding.1014–17

The development of light-cured RMGIC has allowed orthodontists to take advantage of the positive features of conventional glass ionomers, combining them with the mechanical and physical properties of composites. The manufacturer of Fuji Ortho LC (FOLC, GC Corporation, Tokyo, Japan), reports that RMGIC can be used in a moistened environment with no acid etching and obtain clinically acceptable bond strengths. This was verified by Silverman et al2 in a clinical study. These features would save chair time and allow a safe debonding without enamel damage.14

However, besides the improvement achieved by the combination of resin composites, the resin-reinforced GICs still have a lower shear bond strength.3101819 Gaworski et al3 verified a failure rate of 24.8% for RMGIC. Some investigators have evaluated various methods to increase RMGIC bond strength, such as using different enamel conditioners and concentrations for different periods of time and increasing the light curing time.20–22

Therefore, the purpose of this in vitro study was to evaluate three different enamel pretreatments: (1) etching with 10% polyacrylic acid; (2) etching with 37% phosphoric acid; and (3) no acid etching on the shear bond strength of commercially available RMGIC in a saliva-contaminated environment.

MATERIALS AND METHODS

A total of 125 freshly extracted, bovine permanent inferior incisors that had been stored in a 0.1% thymol solution were freed of soft tissues, the pulp removed, and the root sectioned in the middle third. The teeth were stored in room-temperature distilled water.

The crowns of all samples were embedded in acrylic resin and the buccal surfaces wet ground until a 5 mm-diameter flat area was obtained. The roots were embedded in a plastic mold with acrylic resin. Each tooth was oriented so the bonding area would be parallel to the force applied during the shear strength test through an “L” acrylic appliance.

The samples were randomly divided into five groups (Table 1). The bonding area was cleaned with a mixture of distilled water and fluoride-free pumice powder, with a rubber polishing cup in a low-speed handpiece for 10 seconds, rinsed with distilled water for 15 seconds, and dried with oil-free compressed air (MS Compact) for 15 seconds.

TABLE 1.  Groups Description According to Enamel Pretreatment

View Fullscreen

RESULTS

The descriptive statistics for the shear bond strength for different enamel pretreatments are presented in Table 2. A one-way analysis of variance test comparing the five experimental groups revealed significant differences between the mean MPa values (P ≤ .05). The Tukey's HSD method showed no statistically significant differences between mean bond strength values for groups I, III, and IV. On the other hand, the groups where enamel was pretreated with a 37% phosphoric acid (groups II and V) showed higher shear bond strength values, with no statistically significant difference between them.

TABLE 2.  Descriptive Statistics for the In Vitro Shear Bond Strength Test in MPa

View Fullscreen

The relative frequencies of ARI scores for the five experimental groups are shown in Figure 1. Kruskal-Wallis indicated that there were statistically significant ARI differences between group III and all other groups. Spearman's test verified that there was no correlation between shear bond strength and ARI (P ≤ .05).

View Figure

• Download as Powerpoint
• Download Figure

DISCUSSION

Some previous studies have shown that humidity does not reduce the bond strength of FOLCs.14202425 Others have reported that humidity even increases it.82627 Jobalia et al8 reported that FOLC needs a moistened environment to achieve acceptable bond strength, but Chung et al28 reported that this material needs dry enamel to obtain clinically acceptable bond strengths.

The results of this study indicated that the presence of saliva does not significantly decrease FOLC bond strength. Although group I was contaminated with saliva, it had a lower, but not statistically significant, shear bond strength (2.86 MPa) than group IV (3.22 MPa), which was not contaminated. The saliva did not influence FOLC's bond strength, as verified in previous studies.14202425

One of these studies that had also verified that saliva does not influence FOLC's bond strength was carried out by Itoh et al,24 who compared the effects of saliva and water contamination on FOLC's bond strength. The authors observed that saliva had a less deleterious effect on bond strength than water, despite the fact that they were expecting the opposite. According to Mojon et al,29 this happens because some components from natural or artificial saliva protect the cement cure reaction and compensate for the deleterious effects of the water contained in saliva.

It has been reported that it is necessary to condition the moistened enamel before the bonding procedure with FOLC, but some studies have verified that this material achieves clinically acceptable bond strength with no previous acid conditioning.814252730 Silverman et al2 reported a success rate of 96.8% for FOLC in a saliva-moistened environment with no acid etching. On the other hand, Bishara et al20 concluded that when the enamel was unetched, the shear bond strength of FOLC is reduced by half, and this bond strength might not be enough for clinical use.

This study verified that in the presence of saliva, enamel conditioning with 10% polyacrylic acid did not increase FOLC's shear bond strength. Newman et al31 also did not verify statistically significant differences between groups bonded with FOLC in a dry field, with or without enamel conditioning with 10% polyacrylic acid.

The reports in the literature are very conflicting regarding the use of FOLC for orthodontic bonding in enamel moistened with saliva and etched with 10% polyacrylic acid. Jobalia et al,8 as in this study, found no statistically significant difference between the mean bond strength for groups contaminated with saliva either with or without previous enamel acid etching. The values, however, were inferior to the control group. Opposite results were obtained by Lippitz et al,32 Kirovski and Madzarova,27 and Coups-Smith et al,33 who observed an increase in FOLC's shear bond strength when the brackets were bonded to moistened enamel with previous 10% polyacrylic acid conditioning.

Meehan et al,18 in agreement with the findings of this study, obtained lower bond strengths for FOLC in groups with no enamel conditioning with 10% polyacrylic acid when compared with a control group (Transbond XT). On the other hand, Flores et al34 claimed that enamel conditioning with 37% phosphoric acid was a critical factor in obtaining adequate adhesion when FOLC is used. This direct relationship between 37% phosphoric acid conditioning and increase in the shear bond strength was also observed in this study.

Cacciafesta et al,35 in agreement with this study, observed a higher increase in FOLC's bond strength after using 37% phosphoric acid than with 10% polyacrylic acid. According to Bishara et al,22 this happens because 37% phosphoric acid produces a qualitatively rougher enamel surface, thus facilitating the penetration of the FOLC resin.

Although Valente et al36 reported that under wet conditions an acceptable bond strength with FOLC is achieved when there is a previous enamel etching, regardless of the acid used or concentration, Flores et al34 and Graf and Jacobi,30 in agreement with this study, verified that the maximum bond strength was achieved when the enamel was pretreated with 37% phosphoric acid. According to Bishara et al,37 when the acid concentration is increased, the bond strength is also increased.

Opposing the majority of the results in the recent literature, Owens and Miller19 verified that in dry enamel conditioned with 37% phosphoric acid, FOLC yielded significantly lower bond strength values when compared with Transbond XT. According to the authors, if bond strength is the primary consideration for choosing a bonding material, a resin composite should be used.

The ARI scores evaluation showed that with acid pretreatment, all groups, regardless of the bonding material used, had an ARI score of 3 in more than 50% of the samples. In group III, where no acid pretreatment was used, the bond failure was mostly at the enamel and bonding material interface. These findings show that the ARI is directly related to the acid etching and not to the saliva contamination or bonding material used. This is in agreement with the affirmation of Bishara et al20 that etching is a critical variable that affects shear bond strength, as well as bond failure location, when FOLC is used.

This study did not attempt to reproduce human oral conditions or to evaluate whether FOLC shows acceptable bond strength for clinical use, as verified by other in vivo studies.2101726 Instead, it was designed to develop an in vitro study, where the environment allows a control of the variables, to quantify and compare FOLC bond strength in enamel contaminated with saliva under different enamel pretreatments. The control bond strength was determined by Transbond XT (3M Unitek, Monrovia, Calif.), a composite resin traditionally used as a control group in orthodontic bonding studies.

Comparisons between absolute results from bonding studies are almost impossible because different methodologies are used. To obtain a better understanding, and as a means of facilitating comparisons between studies, it is suggested that the methodology used in the orthodontic field needs to be standard where bond strength tests are concerned.

CONCLUSIONS

This in vitro study indicated that in enamel contaminated with saliva:

• Enamel pretreatment with 37% phosphoric acid increased FOLC bond strength values, with no statistically significant differences from those obtained with the resin composite Transbond XT, used as a control.

• Etching the enamel surface with 10% polyacrylic acid, or not etching it, yielded the lowest shear bond strength values, with no difference between them.